What’s Die Casting? Processes, Materials, Applications, Costs

Die casting transforms a vision into reality, enabling the precise creation of intricate metal components that are the backbone of today’s leading industries—from automotive to electronics. At its core, this process involves the high-pressure injection of molten metal into finely crafted molds, setting the stage for innovation and design excellence.

This article offers a deep dive into the die casting process, from the strategic cooling of the cast products to its various materials and applications. For those in the manufacturing realm, grasping the full scope of die casting is not just beneficial—it’s essential.

What is Die Casting?

automotive die casts

Die casting is a versatile and efficient metal casting process known for producing geometrically complex metal parts using reusable molds, called dies. This process involves forcing molten metal under high pressure into these molds, a method especially favored for mass-producing components with precision, repeatability, and a high degree of surface finish.

Originating in the mid-19th century, die casting was initially developed to create a movable type for the printing industry, but its potential quickly expanded to other sectors including automotive, aerospace, and electronics. Today, it primarily uses non-ferrous metals, such as aluminum, zinc, and magnesium, making it a cornerstone in the manufacture of a wide range of products, from tiny intricate toys to critical automotive components.

What sets die casting apart from other casting methods is its ability to produce parts with tight tolerances and minimal machining. The economic benefits coupled with the high durability of die-cast parts also make it a preferred choice among manufacturers aiming to reduce material waste and increase productivity.

How Die Casting Works 

die casting process flow chart

The standard mechanism of the manufacturing process involves injecting molten metal into the die mold at a controlled pressure as highlighted below:

Step 1: Mold Preparation

The die mold comes in different sizes and designs. In terms of design and number of cavities, you should consider the following types:  

  • Single cavity molds are the simplest type of die mold, having one cavity and capable of producing one part per cycle.
  • Multiple cavity molds have a more complex design characterized by identical cavities in a single mold. It can produce multiple but identical parts per cycle, hence its use in mass production of a single part.
  • Combination molds have cavities of different designs within the mold. As a result, they are more flexible and can create different types of parts per cycle.
  • Unit mold is a special die mold suitable for making parts with complex geometries without reducing accuracy. Examples are die casting products with cast-in inserts or thin walls.

After fabricating the mold, clean it to remove contaminants that can affect the part quality. Furthermore, preheat it to prevent thermal defects like cracks. Cracks can occur when there is a significant temperature difference between a die mold and liquid metal.

Step 2: Injection Process

Injection depends on whether it is a hot or cold chamber system. For a cold chamber system, melting takes place outside the casting machine. On the other hand, melting takes place inside the hot chamber casting machine. Afterward, inject the material at the right pressure into the die mold.

Step 3: Cooling

Allow the molten metal to cool and solidify to form the final part. Cooling should occur while the die mold is still clamped. Furthermore, depending on the variation of die casting, cooling might occur while maintaining or adding pressure. For example, in pressure die casting, cooling occurs under continuous pressure to prevent shrinkage.

Step 4: Ejection

After complete solidification of the cast, unclamp the die mold to activate the machine’s ejector pins. This will push out the solidified part. Ejecting the part can be easier by lubricating the mold before injection of the molten metal and incorporating a draft angle.

Step 5: Trimming

Die-cast parts undergo trimming to remove flashes and other defects that leave excess materials on the part. Trimming alongside some post-machining processes such as grinding can also be used to ensure a tighter tolerance. Furthermore, die casts can undergo other metal surface treatments for improved mechanical properties, functionalities, and aesthetics.

Types of Die Casting

Die casting has two types: hot and cold chamber die casting, based on the metal melting and injection mechanism. This section gives a simple explanation of the two types:

Hot Chamber Die Casting

hot chamfer die casting

Hot chamber die casting, also known as gooseneck casting, is one of the most prominent methods used in the die casting industry, particularly suited for metals with low melting points, such as zinc, magnesium, and some alloys of aluminum. Characterized by its speed and efficiency, this process involves a furnace that is integral to the casting machine itself, allowing for rapid cycling and increased production throughput.

The procedure begins with a molten metal reservoir connected directly to the die casting machine. A pneumatically powered plunger pushes the molten metal through a gooseneck-shaped tube into the die cavity. This setup not only speeds up the process but also reduces the metal’s exposure to air, significantly minimizing oxidation and facilitating the production of stronger, denser components.

Hot chamber die casting is highly suitable for producing small to medium-sized parts that require detailed features and tight tolerances, such as gears, connectors, and housings for consumer electronics. Its ability to deliver high-quality parts with a good surface finish and dimensional consistency makes it indispensable in industries where volume production and material integrity are paramount.

Cold Chamber Die Casting

cold chamfer die casting

Cold chamber die casting is a vital process used for metals with high melting temperatures, such as aluminum, copper, and their alloys, that cannot be processed in a hot chamber die casting machine without damaging it. This method is crucial for creating components that require the superior strength and thermal properties these metals provide, making it essential in the automotive, aerospace, and heavy machinery industries.

Unlike the hot chamber process, the cold chamber process involves manually ladling molten metal into a cold chamber where a hydraulic or mechanical plunger forces the metal into a die cavity. This separation of the melting process from the press allows for the handling of metals that would otherwise degrade the machine components due to their high melting points.

Cold chamber casting system is especially appreciated for its ability to produce large, sturdy parts with exceptional mechanical properties and a high level of durability. The process also accommodates higher melting temperatures and thus, wider alloy choices, making it flexible and indispensable for producing critical parts that must withstand extreme conditions.

Below is a summary of the difference between hot and cold chamber die casting:

Hot Chamber Die CastingCold Chamber Die CastingMelting occurs inside the casting machineMelting occurs outside the casting machineUses a low pressure (1000psi to 5000psi)Uses a higher pressure (1500psi to 25,000psi)It uses horizontal injectionIt uses horizontal and vertical injectionHigher energy consumption due to continuous heatingLower energy consumption since melting takes place outside the machine.Suitable for high-volume production of small and intricate partsSuitable for large intricate parts

Variations of the Die Casting Process

The manufacturing process has different variations that modify the general template for improved functionality or aesthetic value. They include:

Gravity Die Casting

Gravity casting differs from traditional die casting by using gravity for mold filling. Advantages of the process include reduced energy consumption, waste generation, air entrapment, and high dimensional accuracy. The casting process is applicable in the automotive industry for making structural parts like engine blocks, cylinder heads, pump housing, and gearbox casing.

Pressure Die Casting

Pressure casting is categorized into two types: low pressure die casting (LPDC) and high pressure die casting (HPDC). Each one has advantages based on the filling mechanism. Filling in HPDC occurs at high pressure (1000 psi to 25000 psi), making it fast and suitable for producing thin-walled parts. In LPDC, filling occurs at a low pressure (0.08MPa to 0.1MPa). This prevents air entrapment and makes it suitable for making dimensionally accurate and non-porous parts.

Pressure casting is applicable in high-precision machining. For example, the aerospace and automotive industries use it in making structural parts engine blocks, and cylinder heads, while the electronic industry uses it in making electronic housings.

Vacuum Die Casting

Vacuum casting only differs by using a vacuum to prevent air entrapment. This leads to improved surface finish and dimensional accuracy. The casting process is applicable in the automotive, medical, and aerospace industries. Common parts made include transmission cases, aluminum implants, and brackets.

Squeeze Die Casting

Squeeze castings have advantages such as improved mechanical properties, reduced porosity, and higher dimensional accuracy. Hence, they are common in the automotive industry for making components like suspensions, steering knuckles, and transmissions.

Semisolid Die Casting

Semisolid die casting also known as thixomolding or rheocasting produces parts with tight tolerances and dimensional accuracy. They are applicable in making parts with complex geometries like transmissions, engine mounts, and electronic housings.

mold for die casting

The manufacturing process is suitable for working with non-ferrous materials like aluminum, zinc, and magnesium alloys. Below are the best materials for the process and why you should consider them:

Aluminum Alloys

Aluminum alloys such as alloys 380, 360, 390, and 413 have low viscosity in their molten state which enables them to flow freely during casting. Their mechanical properties highlighted below, make them popular in the automotive, aerospace, and other industries. 

  • Excellent corrosion resistance
  • High strength-to-weight ratio 
  • Excellent EMI and RFI shielding properties
  • Excellent hardness
  • Good stiffness
  • Excellent thermal conductivity
  • Withstand the highest operating temperatures of all the diecast alloys
  • High dimensional stability with thin walls
  • High electrical conductivity
  • Good surface finishing characteristics
  • Full recyclability

Magnesium Alloys

Magnesium alloy’s high fluidity and good castability reduce porosity during die mold filling. Furthermore, die-casting experts prefer them to aluminum alloys because they are better suited for making parts with complex designs and their high corrosion resistance.

A popular magnesium alloy for casting is AZ91D. The alloy is as strong as aluminum and steel but 33% and 75% lighter than both respectively.

Zinc Alloys

Zinc alloy’s high castability, low melting point, and high solidification rate make them another sought-after casting metal.

Commonly alloys used in the zinc die casting process are Zamak #2, #3, #5, #7, ZA8, and ZA27. They have reduced cycle time, extended die longevity, and excellent mechanical properties.


Copper alloy’s inability to crack during rapid cooling and its ability to create parts with fine-grain structures make them another important material in die casting. Moreover, they have high strength, durability, thermal conductivity, etc., usable in different industries.


Pewter consists primarily of tin (90%), copper (2.5%), lead (7.5%), and a small amount of other elements such as antimony. It is a popular casting material due to its low melting points (1700C to 2300C), good flowability, and good corrosion resistance.

Even though it is a good casting material, the presence lead leads to environmental and health concerns. As a result, it has reduced industrial acceptance in modern-day casting.


Lead is a soft malleable material with a low melting point, good corrosion resistance, and low friction. It is combined with other metals such as Tin, however, its high toxicity reduces its industrial applications.

Tin-Based Alloys

Tin-based alloys are soft and ductile metals with a low melting point (2320C). Also, it has good corrosion resistance and flowability making it suitable for metal die casting. Tin is often combined with other metals such as copper and antimony for better mechanical properties.

Design Considerations in Die Casting

Understanding the material, and casting variations, can affect the part’s quality. However, you should also consider the following geometrics features to improve the part’s performance, manufacturability, and cost-effectiveness. 


A draft angle is a slope integrated into the die mold’s vertical directions to facilitate easier part ejection. However, the angle depends on the casting material, surface finish, wall thickness, and geometric complexity.

Avoiding the draft angle during the mold design will cause the part to stick/drag on the die mold during ejection. Consequently, it can damage the part and/or the mold. Incorporating a larger draft angle will increase material usage and manufacturing costs.

Generally, a draft angle of 10 to 20 will improve part ejection. For typical aluminum die casting, the recommended draft angle is 20 per side to accommodate the material’s abrasiveness. Zinc, on the other hand, has a shrinkage rate of 0.7% which you can accommodate in the tool design.

Fillet Radii

Fillet radii are important in part designs where you cannot avoid sharp corners. They reduce stress concentrations at sharp corners, by distributing it evenly throughout the part. The fillet radii depend on the part geometry, casting material, and functional requirements.

A minimum fillet radius of 0.4mm is recommended but is limited to 0.8mm. A large fillet radius will reduce stress but increase material usage and machining costs. On the other hand, a smaller fillet radius may not provide sufficient stress relief.

Parting Line

The parting line is the line where the two mold halves meet. Ensure the parting line is straight. Furthermore, it must be located and orientated to minimize its visibility and not affect part functionality. Factors like part geometry, undercuts, draft, and gating can influence the parting line placement.


Bosses are a feature added to a die-cast that serves as mounting points. They should have a universal wall thickness for maximum strength. When choosing a boss, consider its diameter, height, and wall thickness. An oversized or undersized boss can lead to assembling issues, part distortion, or reduced part strength.


Ribs are thin and raised features that increase a part’s strength without increasing its weight or material usage and they minimize part deflection and improve dimensional stability. Consider the part size, shape, thickness, height-to-width ratio, and spacing when choosing a rib. Using overly thick or thin ribs can lead to sink marks or warping.

Holes and Windows

Properly designed holes and windows serve as ventilation, drainage, or component integration. Designers should consider the hole diameter, depth, and location during incorporation to prevent part defects or functional issues.

Applications and Uses of Die Casting

Die casting is applicable in industries using non-ferrous materials like aluminum, zinc, and magnesium. Examples include:


The aerospace industry uses metal casting to manufacture aircraft engine components like housings and brackets using aluminum alloys (e.g., ADC12, A380) and magnesium alloys (e.g., AZ91D).

The industry relies on the manufacturing process because of its suitability for the materials they work with, e.g., aluminum, magnesium, etc. Furthermore, it ensures dimensional accuracy and is compatible with complex geometries peculiar to the industry.


The automotive industry uses the manufacturing process to make engine components like cylinder heads, transmission housings, blocks, and body parts such as wheel rims and door handles. Examples of automotive die casting materials used in the industry include aluminum alloys (e.g., ADC12, A380), zinc alloys (e.g., ZAMAK), and magnesium alloys (e.g., AZ91D).


It is applicable in making electronics components such as connectors, heat sinks, and housings using aluminum alloys (e.g., ADC12, A380), zinc alloys (e.g., ZAMAK), and magnesium alloys (e.g., AZ91D). The manufacturing process can precisely make parts with complex details which are common to the electronics industry.

Consumer Products

Consumer products such as kitchen appliances, power tools, and other hardware are made using die casting process using aluminum, zinc, and tin alloy. Die casting offers high productivity, mass production, and cost-effectiveness, which are important in manufacturing these products.


The construction industry makes use of the die casting process in making hardware like hinges, window frames, and fixtures. The manufacturing process can produce parts with complex shapes hence it is important when functions and aesthetic appeal are important.

Benefits of Die Casting 

Metal die casting wide industrial application is due to a few benefits over other manufacturing processes. They include:

Excellent Accuracy

It produces parts with high dimensional accuracy. However, the accuracy depends on the type, variation, and the predesigned die-cast mold. For example, die molds made with advanced CNC machines such as the 5-axis CNC machines, can achieve tight tolerances. Furthermore, variations such as LPDC and gravity die casting that promote proper filling of the die are more accurate.

Complex Details

The manufacturing can make parts with complex geometries including cast-in inserts, thin walls, etc. This ability to incorporate complex details into the design allows the production of parts with diverse shapes and functionalities.

Quick Delivery of High Production Volumes

It is a high-volume production process with a low cost per unit part. However, the speed depends on the casting variation and the mold design. For example, high pressure casting is fast due to the high pressure used, and using multiple and combination molds can improve the speed, number, and cost per unit

Smooth Surface Finishes

A cast metal part will have a smooth surface finish especially when using techniques like low pressure casting, gravity casting, and semisolid casting. The pressure ensures proper filling of the die which increases dimensional accuracy and reduces air entrapment which ensures minimal porosity.

Long Mold Life

Dies are usually made from high-quality steel which is tough and can withstand the high pressures and temperatures associated with the die casting process. Steel’s robustness and durability are key to the longevity of the molds.

Limitations and Challenges of Die Casting

Metal die casting also has a few limitations that can determine whether you use it or not. This section will introduce the limitations, and how to get around them.

Applicable Only to Non-Ferrous Metals

It is only suitable for non-ferrous metals with moderate optimal melting points like aluminum, zinc, and magnesium. Ferrous metals like steel and iron have higher melting points that require special equipment to cast them.

High Die Costs

Die molds incur a high manufacturing cost because CNC machining is a high-volume production process and making a die mold is sometimes a single process. Furthermore, the cost is higher when dealing with complex parts and using steel

Susceptibility to Defects

Depending on die casting types and variations, parts are susceptible to defects such as porosity, shrinkage, and surface imperfection. For example, air entrapment occurs in high pressure casting, and can form pores on the part surface. The pores can form blisters during heat treatment and addressing these defects can lead to a higher manufacturing cost due to the extra surface finishing procedure.

Unsuitability for Small Projects

It has a high initial investment cost including set-up cost, mold manufacturing, etc. To get a low cost per unit part, mass production is encouraged. Consequently, the casting process is unsuitable for small-scale projects and one-off part production.

Comparing Die Casting with Other Manufacturing Processes

Die casting can be confused with processes like injection molding and forging. However, they are different as shown in this section:

Difference Between Die Casting and Injection Molding

Die casting vs injection molding is a popular comparison among those new to the manufacturing world. Both use the same injection principle and are suitable for making parts with complex details with excellent surface finish.

However, they differ in the workpiece and the die mold material. Injection molding uses a steel or aluminum mold and is only compatible with plastic polymers while the other is for non-ferrous metals and uses a steel mold. Other differences between both processes are in the table below:

DifferencesDie CastingInjection MoldingProcessMetal injection into a predesigned steel mold under pressureMolten plastic injection into a predesigned steel or aluminum mold under pressureMaterialNon-ferrous metal alloys (e.g., aluminum, zinc, magnesium)Thermoplastic or thermosetting plasticsMold materialsSteelSteel or aluminumCooling timeLonger cooling timesShorter cooling timesProduction SpeedSlowerFasterTooling costHigher die casting tooling costs due to the use of steel moldsLower tooling cost due to the use of aluminum moldsPart costHigher part costs due to longer production timesLower part cost due to faster production times

Differences Between Forging and Die Casting

The main difference between forging and die casting is the use of die mold. Forging involves shaping a heated metal by applying compressive force while the other relies on the injection of molten metal into a predesigned mold. The differences between both metal fabrication are in the table below.

DifferencesForgingDie CastingProcessInvolves shaping the metal by applying compressive forcesInjection of the metal in a molten state into a mold under pressureMaterialSuitable for ferrous and non-ferrous metals e.g., steel and aluminumSuitable for only non-ferrous metals like aluminum, zinc, magnesiumMold MaterialDoes not require a mold. But it uses a dieSteel moldsProduction SpeedSlowerFasterTolerance ControlModerate tolerance  High tolerance control due to the precision mold manufacturing processFinal Part PropertiesImproved mechanical properties due to the forging processMechanical properties depend on the casting material

Selecting the Right Die Casting Service Provider

Die casting is a simple metal fabrication process, but might require little knowledge and experience. As a result, outsourcing to the right service providers such as ours a better approach.

At RapidDirect, our team of engineers has years of experience in die casting services. We are in a better position to advise you on the right die casting process for your project. We are an ISO 9001:2015 certified company with state-of-the-art facilities that guarantee the manufacturing of high-quality parts. Uploading design files on our online platform, you will get a quote and DfM analysis within 12 hours.

Try RapidDirect Now!

All information and uploads are secure and confidential.


Die casting is a metal fabrication process with high dimensional accuracy. This article discusses the casting process, how it works, and compatible materials so you can make a well-informed decision.

Are you looking for a reputable die-casting service provider? Contact us and experience quality manufacturing at a short lead time and competitive price.


Is Die Casting Product Long-Lasting?

Yes, the parts have high longevity. However, longevity depends on the material used and the environment of use. Furthermore, proper maintenance can improve the part’s longevity.

Is Post-Machining Always Required After Die Casting?

No, post-machining depends on the part’s specific requirement. Some parts might require additional machining operations such as grinding for improved surface finish or to achieve a tighter tolerance. Furthermore, the castings can be blank for the next stage of manufacturing.

How Much Does Die Casting Cost?

The cost of casting a part depends on the production volume, material, part complexity, and size. For example, aluminum die casting tooling can cost about £4000 with parts while finished parts cost as low as £0.4. Moreover, it is a high-volume production process and will only be cost-effective when manufacturing a high number of parts.

Can Die Casting Be Used for Prototyping?

No, metal die casting is not ideal for prototyping due to its high tooling cost and longer lead times. Instead, you can use 3D printing or CNC machining for prototyping and use die casting for mass production.

How Does 3D Printing Enhance Die Casting?

3D printing enhances the die casting process because it supports rapid prototyping. As a result, it enables designers to make different mold designs and allow subsequent adjustments.